The effect of microcosmic morphologies of textured Cu surface by nanosecond laser on the inert wetting and reactive wetting, i.e., ethylene glycol/copper and tin/copper wetting systems, was studied by using modified sessile drop methods. To create different surface roughness, the microcosmic morphologies with different spacing of grooves were constructed by nanosecond laser. The results showed that the inert wetting (ethylene glycol/copper) was consistent with Wenzel model, while the reactive wetting results deviated from the model. In Sn/Cu reactive wetting system, the interfacial evolution in the early stage and the pinning of triple line by the precipitated h-Cu6Sn5 caused the rougher surface and the worse final wettability. When the scale of artificial roughness exceeded the roughness that was caused by interfacial reaction after reaching the quasi-equilibrium state at interface, the final wettability could be improved.
[1] R.N. Wenzel, Resistance of solid surfaces to wetting by water, Transactions of the Faraday Society. 28(1936) 988-994.
[2] G. Palasantzas, J. T. M. D. Hosson, Wetting on rough surfaces, Acta Materialia. 49(2001) 3533-3538.
[3] M. Wu, L.L. Chang, L. Zhang, X.B. He, X.H. Qu, Effects of roughness on the wettability of high temperature wetting system, Surface and Coatings Technology. 287(2016) 146-152.
[4] H.Y. Chen, J.K. Peng, L. Fu, X.C. Wang, Solder wetting behavior enhancement via laser-textured surface microcosmic topography, Applied Surface Science. 368(2016) 208-215.
[5] Satyanarayan, K.N. Prabhu, Spreading behavior and evolution of IMCs during reactive wetting of SAC solders on smooth and rough copper substrates, Journal of Electronic Materials. 42(2013) 2696-2707.
[6] P. Shen, H. Fujii, K. Nogi, Effect of temperature and surface roughness on the wettability of boron nitride by molten Al, Journal of Materials Science. 42(2007) 3564-3568.
[7] Y.Y. Chen, J.G. Duh, B.S. Chiou, The effect of substrate surface roughness on the wettability of Sn-Bi solders, Journal of Materials Science: Materials in Electronics. 11(2000) 279-283.
[8] S.J. Hitchcock, N.T. Carroll, M.G. Nicholas, Some effects of substrate roughness on wettability, Journal of Materials Science. 16(1981) 714-732.
[9] W. Tillmann, J. Pfeiffer, L. Wojarski, Influencing Factors on the Reactive Wetting of Cu-Sn-Ti-and Ag-Cu-Ti-Alloys on Silicon Carbide-Microstructural Observations, Effects and Multivariate Modelling, Advances in Science and Technology. 88(2014) 172-177.
[10] R.K. Kramer, J.W. Boley, H.A. Stone, J.C. Weaver, R.J. Wood, Effect of microtextured surface topography on the wetting behavior of eutectic gallium-Indium alloys, Langmuir. 30 (2014) 533-539.
[11] R. Voytovych, F. Robaut, N. Eustathopoulos, The relation between wetting and interfacial chemistry in the CuAgTi/alumina system, Acta Materialia. 54(2006) 2205-2214.
[12] Q.L. Lin, P. Shen, L. Yang, S. Jin, Q. Jiang, Wetting of TiC by molten Al at 1123-1323K, Acta Materialia. 59(2011) 1898-1911.
[13] W. Zhai, W.L. Wang, D.L. Geng, B. Wei, A DSC analysis of thermodynamic properties and solidification characteristics for binary Cu-Sn alloys, Acta Materialia. 60(2012) 6518-6527.
[14] W. Zhai, B. Wei, Direct nucleation and growth of peritectic phase induced by substantial undercooling condition, Materials Letters. 108(2013) 145-148.
[15] R.A. Gagliano, G. Ghosh, Fine, Nucleation kinetics of Cu6Sn5 by reaction of molten tin with a copper substrate, Journal of Electronic Materials. 31(2002) 1195-1202.
[16] N. Dariavach, P. Callahan, J. Liang, R. Fournelle, Intermetallic growth kinetics for Sn-Ag, Sn-Cu, and Sn-Ag-Cu lead-free solders on Cu, Ni, and Fe-42Ni substrates, Journal of Electronic Materials. 35(2006) 1581-1592.